Electroless Ni-Zn-P alloy coatings were obtained on an iron substrate from a sulfate bath at various pH values. The effects of changes in bath pH on alloy composition, morphology, microstructure and corrosion resistance were studied. Scanning electron microscopy was performed to observe the morphological change of the deposits with bath pH. Coating crystallinity was investigated by grazing incidence asymmetric Bragg X-ray diffraction and transmission electron microscopy. A transition from an amorphous to polycrystalline structure was observed on increasing the bath alkalinity, and thus decreasing the phosphorus content of the alloys. A single crystalline phase corresponding to face-centred-cubic nickel was identified in the alloys obtained from a strong alkaline solution. An increase in zinc percentage up to 23% in the deposits does not change the f.c.c. nickel crystalline structure. Corrosion potential and polarization resistance measurements indicated that the corrosion resistance of electroless Ni-Zn-P alloys depends strongly on the microstructure and chemical composition. The deposits obtained at pH 9.0-9.5 and with 11.4-12.5% zinc and 11.8-11.2% phosphorous exhibited the best corrosion resistance.