The Ce-doped BiFeO3 (BFO) nanoparticles (NPs) were synthesized using a facile solgel route with varying Ce concentrations in the range of 15 mol%. Ferroelectric transition temperature was found to shift from 723 degrees C +/- 5 degrees C for pristine BFO NPs to 534 degrees C +/- 3 degrees C for 5 mol% Ce-doped BFO NPs. UVVis absorption spectra of BFO NPs showed a significant blue shift of similar to 100 nm on Ce doping. The Fourier transformed infrared (FTIR) spectrum centered similar to 550 cm(-1) becomes considerably broadened on Ce doping which is due to additional closely spaced vibrational peaks as revealed by the second derivative FTIR analysis. High-frequency EPR measurements indicated that clustering occurs at high dopant levels, and that Fe is present as Fe(3+)corroborating Mossbauer measurements. The values of saturation and remanent magnetization for 3% Ce-doped BFO NPs are 3.03 and 0.49 emu/g, respectively, which are quite significant at room temperature, making it more suitable for technological applications.