Nanosized ZnS particles were prepared under high-gravity environment generated by the rotating packed bed reactor (RPBR) using zinc nitrate solution and hydrogen sulfide gas as raw materials. The effects of experimental conditions such as reactant concentration, reaction temperature, rotating speed of the RPBR and aging time, on the preparation of nanosized ZnS particles were investigated. A set of suitable operating parameters (the aging time of 48 h, concentration of zinc nitrate of 0.1 mol/l, reaction temperature of 45 degreesC and rotating speed of the RPBR of 1500-1800 rotation/min) for the preparation of nanosized ZnS were recommended. Under these optimum conditions, well-dispersed ZnS nanoparticles was obtained. The crystal structure, optical properties, size and morphology of the product were also characterized by XRD, UV-Vis spectrophotometer, and TEM, respectively. Results indicate that the prepared ZnS has a good absorption for light in the wavelength range of 200-330 nm. XRD analysis also shows the prepared ZnS is in a sphalerite crystal phase. The process has great potential of commercialization. (C) 2003 Elsevier Ltd. All rights reserved.