The Rh2MO6 compounds with M = Mo, W and Te were synthesized by solid state reaction. The compounds all crystallize in a rutile-type structure. These compounds would be expected to be diamagnetic insulators if the oxidation states were Rh3+ and M6+. In fact, all show relatively high electronic conductivities with Rh2TeO6 showing the highest electronic conductivity of similar to 500 S/cm at room temperature. Measurable magnetic moments also indicate valence degeneracy between Rh and the M cation. The measured Seebeck coefficients are relatively low and positive indicating hole-type conduction. (C) 2011 Elsevier Ltd. All rights reserved.