Immiscible crystalline NiAg alloy was successfully synthesized by the newly developed sot-gel auto-combustion method. The structure and composition were examined by X-ray diffraction (XRD) and high resolution transmission electron microscope (HRTEM). All evidence supports that homogeneous NiAg alloy with FCC structure was synthesized. The differential thermal analysis and thermogravimetry (DTA-TG) measurement shows that the alloy has a good thermal stability until 315 degrees C. Unusually some extinction planes are observed in the XRD pattern and HRTEM images. The random distribution of atoms and the large difference between Ni and Ag atom form factors should be regarded as the main reasons for the observation of the extinction planes. The quenching like nonequilibrium thermal process in the combustion is taken as the key factor in the synthesis of immiscible alloy. And the addition of ethylene glycol in the precursors is found to benefit the formation of NiAg alloy. (C) 2011 Elsevier Ltd. All rights reserved.