Isothermal melt crystallization of poly(L-lactide) (PLLA) has been studied in the temperature range of 90 to 135 degrees C. A maximum in crystallization kinetic was observed around 105 degrees C. A transition from regime II to regime III is present around 115 degrees C. The crystal morphology is a function of the degree of undercooling. At crystallization temperatures (T-c) below 105 degrees C, further crystallization occurs upon heating; this behavior is not detected for T-c above 110 degrees C. The analysis of the heat capacity increment at glass transition temperature (T-g) and of dielectric properties of PLLA indicates the presence of a fraction of the amorphous phase which does not relax at the T-g, and the amount of this so-called rigid amorphous phase is a function of T-c.