Natural rubber (NR) was blended in various ratios with 29 kinds of tackifier resins, which were prepared from rosin, terpenes, and petroleum. Miscibilities of all the blend systems were illustrated as phase diagrams in our previous articles. From these blend systems, we selected 7 systems having typical phase diagrams [completely miscible, completely immiscible, and lower critical solution temperature (LCST) types] and carried out measurements of probe tack. Probe tack values were measured at various rates of separation and temperatures to obtain master curves. In the case of miscible pressure sensitive adhesives (PSAs) at the condition of measurement, the peak position in the master curve of probe tack shifted to the lower velocity (higher temperature) as the tackifier content increased. On the contrary, immiscible PSAs had much smaller probe tack values than miscible ones and did not give manifest shift of peaks.