The electrical and the optical properties of organic light-emitting devices (OLEDs) fabricated utilizing a 4,4',4 ''-tris(2-methylphenyl-phenylamino)triphenylamine (m-MTDATA) were investigated to clarify the effect of exciplex on their color stabilization and color purity. The electrons combined with the holes at heterointerfaces between the m-MTDATA layer and the 9,10-di(2-naphthyl)anthracene (MADN) and the 4-(dicyanomethylene)-2-methyl-6-(p-dimethyl aminostyryl)-4H-pyran (DCM1) emitting layer (EML) resulted in the formation of the exciplex. The emission peak of the electroluminescence spectra for the OLEDs fabricated utilizing the m-MTDATA layer shifted to a lower energy side in comparison with that of the EML This was due to the interaction of the holes in the m-MTDATA layer and the electrons in the MADN EML Carriers in white OLEDs (WOLEDs) with exciplex emissions existed at the heterointerfaces between the m-MTDATA and the EML because the DCM1 EML was too thin to affect the EL peak related to the m-MTDATA layer. The Commission Internationale de l'Eclairage coordinates of WOLEDs at 9.5 V were (0.33, 0.36), and their maximum current efficiency at 46 mA/cm(2) was 2.03 cd/A. (C) 2011 Elsevier B.V. All rights reserved.