(111) oriented thin film Pt electrodes were prepared on single crystals of yttrium-stabilized zirconia (YSZ) by sputter deposition of platinum. The electrodes were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected area electron diffraction (SAED), X-ray diffraction (XRD), energy-dispersive X-ray analysis (EDX), atomic force microscopy (AFM) and by profilometry. SEM images of the as-sputtered platinum film show a compact amorphous Pt film covering uniformly the substrate. Upon annealing at 1123 K, gaps and pores at the interface develop leading to a partial dewetting of the Pt film. Increasing the annealing temperature to 1373 K transforms the polycrystalline Pt film into single crystalline grains exhibiting a (111) orientation towards the substrate. (C) 2011 Elsevier B.V. All rights reserved.