The effects of power and pressure on radiofrequency (RF) diode sputtering in oblique-angle (80 degrees) deposition arrangement are presented. Oblique-angle sputtering of ZnO:Ga (GZO) thin films resulted in a tilted columnar crystalline structure and inclination of the c-axis by an angle of approximately 9 degrees with respect to the substrate. This improved their structural, electrical and optical properties in comparison with films deposited perpendicularly to the substrate. GZO films sputtered by an RF power of 600W at room temperature of the substrate in Ar pressure 1.3 Pa showed strong crystalline (002) texture, lowest electrical resistivity 3.4x10(-3) Omega cm, highest electron mobility 10 cm(2) V-1 s(-1), high electron concentration 1.8x10(20) cm(-3) and good optical transparency up to 88%. The small inclination angle of the film structure is caused by the high kinetic energy of sputtered species and additional energetic particle bombardment causes random surface diffusion, which is suppressing the shadow effect produced by oblique-angle sputtering. (C) 2011 Elsevier B. V. All rights reserved.