Polymer(Korea), Vol.37, No.1, 113-120, January, 2013
Export Citation
MMT 첨가에 따른 Polyamide/MMT 나노복합체의 흡습 특성
Effect of MMT on Anti-Water Absorption of Polyamide/MMT Nanocomposites
박상철, 김호겸, 민경은†
  • 경북대학교 고분자공학과
Sang-Cheol Park, Ho-Gyum Kim, and Kyung-Eun Min†
  • Department of Polymer Science, Kyungpook National University, Daegu 702-701, Korea
E-mail:
초록
Pilot scale에서의 나노복합체의 상용화를 위해 용융 삽입법을 적용하고 이축 압출기로 제조한 polyamide/MMT 나노복합체의 흡습 특성을 연구한 결과, MMT 도입으로 수분 흡수율이 감소되었으며 그에 따라 치수 안정성이 향상되었다. 굴곡강도 및 탄성률은 수분 흡수율이 증가함에 따라 저하되었으며, 이로부터 MMT의 도입은 강도 향상효과와 함께 흡습방지를 통한 강도 저하 억제효과도 보이는 것으로 조사되었다.
The melt intercalation to commercialize nanocomposites in a pilot scale was applied and the water absorption characteristics for polyamide/MMT nanocomposites manufactured by twin screw extruder was studied. As a result, water absorption decreased with the introduction of MMT and dimensional stability was improved. However, as water absorption increased, flexural strength and modulus were reduced. Therefore, the effect of MMT introduction on mechanical properties of nanocomposites was clearly observed, which may increase the level of strength by maintaining anti-water absorption property of nanocomposite.
Keywords:polyamide;nanocomposite;water absorption;dimensional stability;flexural.
  1. Monticelli O, Musina Z, Ghigliotti F, Russo S, Causin V, e-Polymers, No.124 (2007)
  2. Usuki A, Kojima Y, Kawasumi M, Okada A, Fukushima Y, Kurauchi T, Kamigaito O, J. Mater. Res., 8, 179 (1993)
  3. Wu SH, Wang FY, Ma CCM, Chang WC, Kuo CT, Kuan HC, Chen WJ, Mater. Lett., 49, 327 (2001)
  4. Uribe-Arocha P, Mehler C, Puskas JE, Altstadt V, Polymer, 44(8), 2441 (2003)
  5. Kashiwagi T, Harris RH, Zhang X, Briber RM, Cipriano BH, Raghavan SR, Awad WH, Shields JR, Polymer, 45(3), 881 (2004)
  6. Mu B, Wang QH, Wang TM, Wang HG, Jian LQ, Polym. Eng. Sci., 48(1), 203 (2008)
  7. Liu X, Wu Q, Macromol. Mater. Eng., 287, 180 (2002)
  8. Chavarria F, Paul DR, Polymer, 45(25), 8501 (2004)
  9. Liu XH, Wu QJ, Macromol. Mater. Eng., 287, 180 (2002)
  10. Mehrabzadeh M, Kamal MR, Polym. Eng. Sci., 44(6), 1152 (2004)
  11. Han B, Ji GD, Wu SS, Shen J, Eur. Polym. J., 39, 1641 (2003)
  12. Shen L, Phang IY, Chen L, Liu TX, Zeng KY, Polymer, 45(10), 3341 (2004)
  13. Vlasveld DPN, Vaidya SG, Bersee HEN, Picken SJ, Polymer, 46(10), 3452 (2005)
  14. Gyoo PM, Venkataramani S, Kim SC, J. Appl. Polym. Sci., 101(3), 1711 (2006)
  15. Lu YL, Zhang Y, Zhang GB, Yang MS, Yan SK, Shen DY, Polymer, 45(26), 8999 (2004)
  16. Yu ZZ, Yang MS, Zhang QX, Zhao CG, Mai YW, J. Polym. Sci. B: Polym. Phys., 41(11), 1234 (2003)
  17. Liu XH, Wu QJ, Berglund LA, Polymer, 43(18), 4967 (2002)
  18. Lu YL, Zhang GB, Feng M, Zhang Y, Yang MS, Shen DY, J. Polym. Sci. B: Polym. Phys., 41(19), 2313 (2003)
  19. Lee SJ, Polym. Sci. Technol., 1(3), 134 (1990)
  20. Hahn MT, Hertzberg RW, Manson JA, Sperling LH, Polymer., 27, 1885 (1986)
  21. Vlasveld DPN, Groenewold J, Bersee HEN, Picken SJ, Polymer, 46(26), 12567 (2005)
  22. Fornes TD, Yoon PJ, Keskkula H, Paul DR, Polymer, 42(25), 9929 (2001)
  23. Yu ZZ, Yan C, Yang M, Mai YW, Polym. Int., 53, 1093 (2004)
  24. Lee SS, Park M, Lim S, Kim J, Hwang JT, Polym. Sci. Technol., 18(1), 8 (2007)
  25. Choi JH, J. KIMST., 9, 88 (2006)
  26. Alexandre B, Langevin D, Mederic P, Aubry T, Couderc H, Nguyen QT, Saiter A, Marais S, J. Membr. Sci., 328(1-2), 186 (2009)
  27. Zhang QX, Yu ZZ, Yang MS, Ma J, Mai YW, J. Polym. Sci. B: Polym. Phys., 41(22), 2861 (2003)
  28. Homminga DS, Goderis B, Mathot VBF, Groeninckx G, Polymer, 47(5), 1630 (2006)
  29. Lin B, Thumen A, Heim HP, Scheel G, Sundararaj U, Polym. Eng. Sci., 49(4), 824 (2009)