Polymer nanocomposite (NC) hydrogels exhibiting both dynamic restructuring and unusual adhesive properties in wet and dry states have been prepared in an efficient and straightforward way via free radical polymerization of poly(ethylene glycol) methyl ether acrylate (PEG) in the presence of silane-modified sodium montmorillonite (NaMMT). The dynamic restructuring of the NC gel has been demonstrated by almost instant recovery of mechanical properties, such as storage modulus, loss modulus, and damping tan delta (at 0.025 strain) by 60-110% after being stressed to the point of gel failure. Furthermore, the dry NC gel showed exceptional thermal and mechanical stability during a heating and cooling cycle between 25 and 110 degrees C, with only slightly decreases followed by at least 30% increases in both moduli, while tan delta remained nearly unchanged. The NC gel in dry state could repeatedly adhere to various surfaces such as steel, glass, plastic, etc and detach from the surface without being broken and leaving little contamination behind. This unique adhesive characteristic was characterized by high storage modulus, loss modulus (kPa), and tan delta (>0.6) corresponding to high cohesive, adhesive, and tacking properties of pressure sensitive adhesives (PSAs). Finally, a reversible network structure formed by PEO interpenetrating within 3-dimentional (3-D) silica network was proposed to be responsible for the dynamic restructuring and the unique adhesive behaviors observed in the NC gel, and the 3-D network structure was investigated by XRD, FTIR, and DSC measurements. For this 3-D network structure, we suggest that the flexibility of PEO could allow PEO side chains to contact with various surfaces by either PEO segments or methoxy end groups via weak physical interactions, such as van der Waals interactions or hydrogen bonding, whereas the reversible network structure contributes to the recovery of strength and shape after the gel failure.