In this paper, the reduction degree of graphene oxide (GO) reduced using chemical reduction and thermal reduction methods was characterized by spectrum analysis. The optimized conditions of reducing GO were determined that the hydrazine hydrate is the best reducing agent and the appropriate thermal reduction temperature is at 240 degrees C. The obtained GO solution was mixed with polystyrene (PS) solution to prepare PS/r-GO composites by using two-step reduction technique under the optimized conditions. The structure and micro-morphology of GO, r-GO and PS/r-GO composites were characterized by Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), Scanning electron microscopy (SEM), Transmission electron microscopy (TEM) respectively. It is also observed that the two-step reduction pathway is more effective than one-step reduction for improving the reduction degree of GO. Accordingly, the electric conductivity of PS/r-GO composites prepared by two-step reduction technique is as high as 21.45 S m(-1), which is much higher than that of composites fabricated by one-step reduction method. The spectrum techniques will highlight new opportunities for investigating the reduction degree of GO in polymer composites. (C) 2013 Elsevier B.V. All rights reserved.