Alumina-supported In2O3, Ga2O3 and B2O3 were investigated as catalysts for lean NOx reduction with DME as reducing agent and compared to pure Al2O3 and In2O3. The In2O3-promoted alumina catalysts showed the highest NOx conversion at low temperatures, although with a narrow temperature window. Pure In2O3, on the other hand, was inactive for NOx reduction with DME. The Ga2O3- and B2O3-promoted alumina catalysts gave the highest NOx conversion at higher temperatures, showed a temperature window similar to pure alumina, but were less sensitive to H2O inhibition. Possible reasons for these observations are discussed. (c) 2012 Elsevier B.V. All rights reserved.