This paper evaluates the influence of the hydrothermal treatment temperature on the phase formation, structure and photocatalytic potential of Nb2O5 nanoparticles obtained by the oxidant-peroxo method (OPM). The materials were characterized by X-ray diffraction (XRD), Raman spectroscopy, UV-vis diffuse reflectance spectroscopy (DRS), scanning and transmission electron microscopy (SEM and TEM), thermogravimetry (TGA), Fourier transform infrared spectrometry (FTIR) and N-2 adsorption isotherms. The photocatalytic efficiency of the Nb2O5 nanoparticles and the mechanism of degradation were evaluated with respect to the degradation of the contaminants: rhodamine B (RhB) and atrazine under UV and visible radiation. The synthesized nanoparticles presented mixed phases of Nb2O5 orthorhombic and Nb2O5 center dot nH(2)O, with particle size ranging from 30 to 40 nm and specific surface area ranging from 129 to 199 m(2)/g. The results showed that the nanoparticles can be applied as catalysts for photoactivated reactions. The rate constant of RhB photodegradation in the reaction catalyzed by the Nb2O5 samples was approximately 5 times higher than the rate observed for RhB direct photolysis (RhB self-photolysis), and approximately 2 times higher than RhB photodegradation catalyzed by TiO2 (reference). The surface hydroxylation and crystallinity were the most important parameters for the photoactivity per unit area of the Nb2O5 nanoparticles obtained at lower (100 and 125 degrees C) and higher (150 and 175 degrees C) hydrothermal temperatures, respectively. Furthermore, under UV radiation, the main photodegradation mechanism occurred by the attack of center dot OH radicals on the molecules (RhB and atrazine) and not by the direct oxidation of adsorbed molecules on the photocatalyst surface. Dye-sensitized photocatalysis was the main mechanism for RhB degradation under visible radiation. (C) 2013 Elsevier B.V. All rights reserved.