Surface and structural properties of the laser irradiated titanium targets have been investigated under dry and wet ambient environments. For this purpose KrF Excimer laser of wavelength 248 nm, pulse duration of 20 ns and repetition rate of 20 Hz has been employed. The targets were exposed for various number of laser pulses ranging from 500 to 2000 in the ambient environment of air, de-ionized water and propanol at a fluence of 3.6 J/cm(2). The surface morphology, chemical composition and crystallographical analysis were performed by using Scanning Electron Microscope (SEM), Energy Dispersive X-ray Spectroscopy (EDS) and X-ray Diffraction (XRD), respectively. For both central and peripheral ablated areas, significant difference in surface morphology has been observed in case of dry and wet ambient conditions. Large sized and diffused grains are observed in case of dry ablation. Whereas, in case of wet ablation, small sized, and well defined grains with distinct grain boundaries and significantly enhanced density are revealed. This difference is ascribed to the confinement effects of the liquid. The peripheral ablated area shows redeposition in case of dry ablation whereas small sized grain like structures are formed in case of wet ablation. EDS analysis exhibits variation in chemical composition under both ambient conditions. When the targets are treated in air environment, enhancement of the oxygen as well as nitrogen content is observed while in case of de-ionized water and propanol only increase in content of oxygen is observed. X-ray diffraction analysis exhibits formation of oxides and nitrides in case of air, whereas, in case of de-ionized water and propanol only oxides along with hydrides are formed. For various number of laser pulses the variation in the peak intensity, crystallinity and d-spacing is observed under both ambient conditions. (c) 2012 Elsevier B.V. All rights reserved.