The corrosion inhibition effects of an imidazolium-based task specific ionic liquid (TSIL) were investigated on a low carbon steel in 1 M HC1 solution. Samples were exposed to 1 M HC1 solution without and with different concentrations of TSIL. Weight loss measurements, potentiodynamic polarization test, electrochemical impedance spectroscopy (EIS), scanning electron microscope (SEM), atomic force microscope (AFM) and contact angle measurements were utilized to investigate the inhibition effects of TSIL. The results obtained from the polarization studies revealed that both the anodic and cathodic branches slopes affected in the presence of TSIL. It was shown that TSIL behaved as a mixed type inhibitor with a dominant effect on the anodic reaction rate depression. It was shown that the increase in polarization resistance and the decrease in corrosion current density were more pronounced using 100 mg/L of TSIL after 2 h immersion time. It was also shown that the adsorption of TSIL followed a Langmuir adsorption isotherm. (C) 2013 Elsevier B.V. All rights reserved.