Hydroxyapatite (HA) coatings in and onto anodized TiO2 nanotube arrays were presented and prepared by electrophoretic deposition technique (EPD). Coatings were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). EPD proved to be an innovative and versatile technique to coat HA on and into nanotubular structures of TiO2 with enhanced adhesion between nanotubes and HA particles provided by mechanical interlocking. After EPD of HA on TiO2 layer, samples were sintered at 400 degrees C, 600 degrees C and 800 degrees C for 2 h in an Ar atmosphere. Effect of EPD processing parameters on thickness of the deposits and rate of deposition was elucidated for HA coatings on the nanotubular TiO2 structures. It was shown that higher applied voltages increase deposition rate and thickness of the coatings. Potentiodynamic polarization measurements proved corrosion protection caused by both HA coating and nanotubular TiO2 structure in simulated body fluid (SBF). Effect of sintering temperature on adhesion strength of HA coatings on TiO2 nanotubes and their composition were also studied. (C) 2014 Elsevier B.V. All rights reserved.