Calcium based CO2 solid sorbents reveal a different efficiency of the carbonation/calcination cycle according to their origin, natural or synthetic, and the synthesis method. The objective of this research was to develop high-performance sorbents for CO2 capture at high temperature by using a supercritical method to precipitate CaCO3 precursors. Two different sorbents were synthesized: micrometric particles of CaCO3 surrounding Ca(OH)(2) and nanometric calcite with a CaO core. Results were compared with atmospherically precipitated calcium carbonate. Capture performance of produced materials was tested in a magnetic microbalance under mild calcination conditions (750 degrees C and N-2) and at 900 degrees C under CO2 pressure. Further, tubular furnace treated samples under the mild carbonation conditions (700 degrees C and N-2) were used to perform an extensive investigation on the morphological and textural characteristics of calcined and carbonated samples. At a calcination temperature of 750 degrees C, an enhanced reversibility of the reaction and faster kinetics were observed for the supercritically prepared micrometric sample compared to the other two studied materials. After 25 cycles, this micrometric sample has one of the highest values of residual carbonation conversion described in the literature. At 900 degrees C calcination temperature and in the presence of CO2, severe sintering occurred in both micrometric and nanometric materials and similar conversion values were recorded for the two supercritically prepared samples. Nevertheless, these sorbents still have a residual conversion value two times higher than that of natural limestone. (C) 2013 Elsevier B.V. All rights reserved.