This paper mainly focuses on the preparation, characterization, thermal properties and thermal stability and reliability of new form-stable composite phase change materials (PCMs) prepared by vacuum impregnation of paraffin within graphene oxide (GO) sheets. SEM and FT-IR techniques and TGA and DSC analysis are used for characterization of material and thermal properties. The composite PCM contained 48.3 wt.% of paraffin without leakage of melted PCM and therefore this composite found to be a form-stable composite PCM. SEM results indicate that the paraffin bounded into the pores of GO. FT-IR analysis showed there was no chemical reaction between paraffin and GO. Temperatures of melting and freezing and latent heats of the composite were 53.57 and 44.59 degrees C and 63.76 and 64.89 kJ/kg, respectively. Thermal cycling tests were done by 2500 melting/freezing cycling for verification of the form-stable composite PCM in terms of thermal reliability and chemical stability. Thermal conductivity of the composite PCM was highly improved from 0.305 to 0.985 (W/mk). As a result, the prepared paraffin/GO composite is appropriate PCM for thermal energy storage applications because of their acceptable thermal properties, good thermal reliability, chemical stability and thermal conductivities. (C) 2012 Elsevier Ltd. All rights reserved.