Sequential adsorption of CO and NO as well as equimolar NO + CO reaction with variation of temperature over Pd2+ ion-substituted CeO2 and Ce0.75Sn0.25O2 supports has been studied by DRIFTS technique. The results are compared with 2 at.% Pd/Al2O3 containing Pd-0. Both linear and bridging Pd-0-CO bands are observed over 2 at.% Pd/Al2O3. But, band positions are shifted to higher frequencies in Ce0.98Pd0.02O2-delta and Ce0.73Sn0.25Pd0.02O2-delta catalysts that could be associated with Pd delta+-CO species. In contrast, a Pd2+-CO band at 2160 cm(-1) is observed upon CO adsorption over Ce0.98Pd0.02O2-delta and Ce0.73Sn0.25Pd0.02O2-delta catalysts pre-adsorbed with NO and a Pd+-CO band at 2120 cm(-1) is slowly developed on Ce(0.73)Srl(0.25)Pd(0.02)O(2-delta) over time. An intense linear Pd-0-NO band at 1750 cm(-1) found upon NO exposure to CO pre-adsorbed 2 at.% Pd/Al2O3 indicates molecular adsorption of NO. On the other hand, a weak Pd2+-NO band at 1850 cm(-1) is noticed after NO exposure to Ce0.98Pd0.02O2-delta catalyst pre-adsorbed with CO indicating dissociative adsorption of NO which is crucial for NO reduction. Pd-0-NO band is initially formed over CO pre-adsorbed Ce0.73Sn0.25Pd0.02O2-delta which is red-shifted over time along with formation of Pd2+-NO band. Several intense bands related to nitrates and nitrites are observed after exposure of NO to fresh as well as CO pre-adsorbed Ce0.98Pd0.02O2-delta and Ce0.73Sn0.25Pd0.02O2-delta catalysts. Ramping the temperature in a DRIFTS cell upon NO and CO adsorption shows the formation of N2O and NCO surface species, and N2O-formation temperature is comparable with the reaction done in a reactor. (c) 2013 Elsevier Inc. All rights reserved.