Surface dilational moduli of poly (ethylene oxide) (PEO), poly (methyl methacrylate) (PMMA), and compatible PEO/PMMA blend films spread at the air-water interface were investigated as a function of surface concentration. The surface dilational modulus of an expanded PEO film increased as the surface concentration increased to 0.4 mg/m(2), which corresponds to the limiting surface area of PEO. After peaking at this value, the surface dilational modulus decreased with an increase in the PEO concentration. Lissajous orbits of PEO films exhibited positive hysteresis loops for all surface concentration ranges. On the other hand, the surface dilational modulus of a condensed PMMA film steeply increased as the surface concentration increased. Lissajous orbits of PMMA films changed from positive hysteresis loops to negative loops at the surface concentration at which the surface pressure reached in the plateau region. The magnitude of the surface dilational modulus of PMMA was larger than that of PEO at a fixed surface concentration. The surface dilational moduli of the PEO/PMMA blend films increased with the total surface concentration and their magnitudes were less than those of the individual PMMA films and larger than those of the individual PEO films at fixed surface concentrations. Lissajous orbits of the PEO/PMMA blend films also changed from positive hysteresis loops to negative loops beyond the surface concentration at which the plateau surface pressure of PEO was attained. (C) 2012 Elsevier Inc. All rights reserved.