The rheological properties at small (oscillatory shear) and large (uniaxial compression) deformations of heat-induced gels (80 degrees C for 20 min, pH 7.3) containing 25% rennet casein (RCN), 2.5% disodium phosphate and 0%, 2.3% or 6.3% of whey protein isolate (WPI) were measured for samples cooked in a torque-rheometer at mixing speeds within a range of 20-200 rpm (shear rates: similar to 15-230 s(-1)). In addition, microstructure analyses were performed, separately staining RCN and WPI, by Confocal Scanning Laser Microscopy (CSLM). Both small and large deformation tests indicated that increasing addition of WPI prior to the cooking process of RCN resulted in gels exhibiting higher storage and deformability moduli than WPI-free samples. Increasing shear rates during cooking also affected the theological properties of RCN-WPI gels, and stronger gels were formed as the shear rate during cooking was increased. Despite the data dispersion among replicates, the effect of shear rate on gel strength were evident for RCN gels with 6.3% WPI and relatively clear for gels with 2.3% WPI: however, the trend was uncertain for WPI-free RCN gels. Possible explanations for this observation are that when increasing WPI levels in the presence of RCN and heat, disulfide-thiol exchange reactions between denatured WPI and kappa-casein (kappa-CN) are increased and possibly promoted by shear rate, resulting in stronger and more cross-linked gel structure. CSLM results were not conclusive to support this hypothesis. (C) 2010 Elsevier Ltd. All rights reserved.