Because of the ubiquity of polychlorinated dibenzo-p-dioxins and dibenzofurans (PCDD/Fs) in kaolinitic clays, the ceramic industry is considered to be a potential source of PCDD/Fs. However, studies on the emission of PCDD/Fs from ceramic production are still very scarce. In this study, PCDD/Fs emissions during ceramic production were investigated in an electric laboratory batch kiln. The results showed that the PCDD/Fs were completely removed from the ceramic pieces after 30 min of firing at the peak temperature of 1200 degrees C. Nevertheless, on the mass and international toxic equivalent basis, 27.5% and 46.2% of the total PCDD/Fs amount in the raw clay were released into the atmosphere during firing, respectively. These PCDD/Fs were emitted into the air before the temperature was elevated to a level high enough for their destruction. Dechlorination reactions generated a broad distribution within the PCDD/Fs congeners including a variety of non-2,3,7,8-substituted ones. The emission of PCDD/Fs was decreased to 16.3 wt.% of the total PCDD/Fs amount in the raw clay, when the initial kiln temperature was enhanced to 600 degrees C. The emission of PCDD/Fs could be reduced significantly in the presence of a glaze coating on the ceramic test piece. These results indicated that ceramic production is an un-neglectable source of PCDD/Fs in the environment. (C) 2012 Elsevier B.V. All rights reserved.