9-tert-Butylanthracene undergoes a photochemical reaction to form its strained Dewar isomer, which thermally back-reacts to reform the original molecule. When 9-tert-butylanthracene is dissolved in a polymer host, we find that both the forward and reverse isomerization rates are pressure-dependent. The forward photoreaction rate, which reflects the sum of contributions from photoperoxidation and Dewar isomerization, decreases by a factor of 1000 at high pressure (1.5 GPa). The back-reaction rate, on the other hand, increases by a factor of similar to 3 at high pressure. Despite being highly strained and higher volume, the back-reaction reaction rate of the Dewar isomer is at least 100x less sensitive to pressure than that of the bi(anthracene-9,10-dimethylene) photodimer studied previously by our group. These results suggest that the high pressure sensitivity of the bi(anthracene-9,10-dimethylene) photodimer reaction is not just due to the presence of strained four-membered rings but instead relies on the unique molecular geometry of this molecule.