Guest host nonlinear optical polymers have attracted considerable interest due to their applications in fast electro-optical modulators and wavelength converters. In general, the electrical poling procedures, for which high DC external fields are applied, are necessary for aligning guest chromophores in polar order and activating the second-order nonlinearity. We present the nonelectrical poling behaviors for guest host polymers: DR1 (4-[ethyl (2-hydroxyethyl) amino]-4'-nitroazobenzene) is the guest, and PMMA (poly (methyl methacrylate)) is the host. Second-order nonlinear optical susceptibility was induced in the conventional guest host polymers after annealing at temperatures above the glass transition points of the host polymer even without applying the external fields. This phenomenon did not occur in the side-chain polymers, where the guests were directly bonded to the host chains. The guest polar alignments were most likely generated from the guest hydroxyl groups chemisorbing on the substrates. The polar alignments of the guest formed not only near the surface of the substrate, but also inside the host polymers. The optimized conditions for the SHG conversion were examined in the context of the polymer film thickness and guest concentration. The nonelectrical poling techniques described in this study are useful for enhancing the surface nonlinearity in the several materials, and they will be useful for further developments in nanophotonics and plasmonics.