Homogeneous substitution of Cu(II), AI(III) and Ti(IV) for Mn in the spinel Li[Mn-2]O-4 is synthesized by lactic-acid assisted Pechini method. Galvanostatic charge-discharge between 3.5 and 4.3 V (versus Li+/Li) at C/2 rate shows that the multi-cations doped spinel exhibits initial discharge capacity of 134 mAh g(-1) with a 97% capacity retention after 400 cycles at room temperature. When cycling at 55 degrees C, the doped sample shows 91% capacity retention after 50 cycles compared to 70% retention for the undoped sample. As the charge-discharge rate increases to 12C, the doped sample delivers capacity of 111 mAh g(-1), which is much higher than that of the undoped sample of only 84 mAh g(-1). Moreover, as the charge-discharge rate returns from 12C to C12, the discharge capacity of the doped electrode recovers nearly completely while the undoped sample lost more than 7% of its capacity. (C) 2011 Elsevier B.V. All rights reserved.