Low temperature (LT) metal supported solid oxide fuel cells (SOFCs) have many advantages in comparison to conventional electrode or electrolyte supported type SOFCs. NRC has demonstrated high performance LT metal supported planar SOFCs fabricated by either wet colloidal spray/sintering or suspension thermal spray. The combination of tubular configuration and metal supported SOFCs may produce more unique and very attractive advantages such as easy and inexpensive sealing method and materials, high specific and volumetric power density, cost-effective fabrication, enhanced robustness, rapid start up, red-ox cycle tolerance and potential use for a pressurized integrated system. In this paper, thin film solid electrolyte of Sm0.2Ce0.8O1.90 (SDC) and NiO-SDC composite anode on sintered porous tubular metal supports were deposited by suspension HVOF spray and suspension plasma spray, respectively on sintered porous tubular metal support. La0.6Sr0.4Co0.2Fe0.8O3-delta (LSCF) cathode on the SDC electrolyte was formed by wet colloidal spray and subsequent sintering process as the final fabrication step. The detailed investigation of suspension and process-related parameters for suspension thermal spray was performed in order to produce thin and crack-free SDC thin film coatings. The electrochemical performance of single cells was demonstrated. Crown Copyright (C) 2012 Published by Elsevier B.V. All rights reserved.