Solvent method was used to recover LiCoO2 scrap materials, and the effects of heat treatment on the scrap materials for Li-ion battery were investigated in detail. SEM results showed that heat treatment could slightly reduce the degree agglomeration of the scrap materials. XRD results showed that the layer structure of LiCoO2 was partly destroyed during the recovery process. Low temperature heat treatment could contribute to restore the original layer structure of LiCoO2, however, high temperature heat treatment could lead to the further damage of the layer structure. Compared with the unheat-treated scrap materials, the discharge capacity and the cycle life of the pristine scrap materials heat-treated at 200 degrees C, 250 degrees C and 300 degrees C were obviously improved, Especially after heat-treated at 250 degrees C, the discharge capacity could reach about 154.6 mAh g(-1) and the capacity retention rate still remained at 92.0% after 360 cycles. Particle size distribution, tap density and recovery rate of scrap materials were also investigated. (C) 2013 Elsevier B.V. All rights reserved.