Since the chemical/electrical stability and catalytic activity are essential conditions for catalyst counter electrodes (CCEs) in dye-sensitized solar cells (DSSCs), a simple dipping method is employed for evaluating the chemical stability of CCE candidates in an iodine-based liquid electrolyte (I-electrolyte). The chemical stabilities and transition mechanisms of the CCEs are successfully analyzed by studying the chemical transitions in X ray photoelectron spectroscopy (XPS) core levels after dipping in the I-electrolyte. All films including the Pt film undergo degradation depending on the type of material. While dipping in the I-electrolyte, Cu and Au films scarcely dissolves as their respective metal sulfides, and the Al film gradually loss its metallic properties owing to Al2O3 growth. On the other hand, a previously unknown transition mechanism of organic conducting CCEs is determined based on the proposed method. Compared to the other metal films, the poly(3,4 ethylenedioxythiophene) poly(styrenesulfonate) (PEDOT:PSS) and multi wall carbon nanotube (MWCNT)/PEDOT:PSS films undergo an entirely unique transition mechanism, which results from the chemical adsorption of organic molecules onto PEDOT:PSS molecules in the I-electrolyte. Consequently, these chemical structure transitions correspond well to the degrees of alternation in the electrical properties of DSSCs with all the investigated CCEs. (C) 2014 Elsevier B.V. All rights reserved.