Nanograins of SmCoO3 are prepared by citric acid assisted Sol-Gel autocombustion route. The characterizations of crystal structure, surface morphology and electrical properties of SmCoO3 powder are done using XRD, HRSEM, FTIR and BDS. The structural evolution of SmCoO3 upon increasing the annealing temperature is followed using XRD and FTIR analyses. The powder sample contains polycrystalline grains with average size equal to 35 nm and orthorhombic perovs.kite structure with Pbnm space group. The vibrational bands observed in FTIR spectrum at 545 cm(-1) and 439 cm(-1) correspond to Co-O stretching modes in cobaltite system. HRSEM images of the sample show the formation of hexagonal shaped grains of samarium cobaltite. The AC electrical conductivity of 4.914 Chi 10(-5) S cm(-1) at 295 K is measured for SmCoO3 nanoparticles. The impedance spectra bring out the semiconducting behavior of the material. (C) 2014 Elsevier Ltd. All rights reserved.