The effect of helium on irradiation damage behavior in Fe-Cr-Mn(W,V) steel was investigated by electron/helium ion dual-beam irradiation. The results indicate that helium can promote the increase of dislocation density and enhance the void nucleation and void swelling of Fe-Cr-Mn(W, V) alloy. The segregation of solute elements near grain boundary was suppressed by existence of helium. Also the interface of carbide-matrix migration and the change of solute concentration near the interface were observed during dual-beam irradiation.