The microstructural changes and the relations between mechanical properties and additive powder with various brazing temperatures and times were investigated. The IN738 and BNi-3 alloy powders were used as an additive and filler metal powders for the brazing process. The wide-gap brazing process was carried out in a vacuum of 2 x 10(-5) torr. The wide-gap region brazed with 60wt.% IN738 additive powder had a microstructure consisting of IN738 additive, and binary eutectic of Ni3B-Ni, and (Cr, W)B. As the brazing temperature and time were increased, the size of IN738 additive powder increased to 181 mu m, which decreased the amount of low strength Ni3B-Ni eutectic structure, thereby increasing the fracture strength of the wide-gap brazed region. Cracks in the brazed region were observed to propagate through the Ni3B-Ni structure, which lowered the fracture strength of the wide-gap brazed region.