A phosphate conversion coating was deposited on diecast AZ9ID magnesium alloys, the film was a complex phosphate containing Mg and Al, which showed amorphous structure. Corrosion resistance of conversion coating in 3.5%NaCl was investigated by polarization curve. It was showed that the anodic branch of polarization curve for the phosphate conversion coating presented typical passivation characteristic. Immersion test results showed that the corrosion rate of phosphate conversion coating was less than that of chromate Dow7 film.