Magnetic annealing at five different magnitudes of field was conducted to evaluate the effect of the field on the recrystallized microstructure of Fe-0.75%Si samples. At higher fields the retardation during recrystallization is compensated by the magnetic filed driving force that causes an increase in the grain boundary mobility of grains that have a certain relationship with the direction of the field