Induced defects in silver polycrystalline samples irradiated with 4 keV Ar(+) were characterised with slow positron implantation spectroscopy. The implanted gas was found to interact with ion irradiation defects. The evolution of the defects and gas-defect interactions were followed through a multi-step isochronal annealing treatment. Two different defected regions were detected. A region near to the surface, due to a distribution of vacancy-like defects produced by irradiation, and a deeper one due to coalescence of Ar. The deeper defects evolve with thermal treatments and probably produce cavities which are not easily recovered.