This paper described new characterization methods and data to quantify the influence of solute atoms on grain boundary and sub-grain boundary mobilities in Al-Mn alloys with a view to their integration into recovery and recrystallization modelling. Detailed SEM measurements of grain boundary mobilities during recrystallization have been made by in-situ annealing experiments on cold deformed Al-0.1 and 0.3wt.% Mn binary alloys. Stored energies are estimated from the sub-grain sizes and misorientations and the boundary velocities directly measured in the temperature range 200-450 degrees C. It is shown that in many cases good agreement with the Cahn, Lucke, Stuwe model for solute drag is obtained, e.g. the activation energies are intermediate between those of boundary and volume solute diffusion. Some particular cases of rapid growth occur in Al-0.1%Mn indicating boundary breakaway from solute clouds. A complementary study of sub-grain boundary mobilities has started on the same alloys; in this case the average mobilities are estimated from FEG-SEM growth data for the average sub-grain size for temperatures in the range 150-300 degrees C. The results are compared with some previous data on Al-Si and show similar rates.