In this study, the different silane coupling agents were added to epoxy/silica systems. The effects of the type of silane coupling agent in the epoxy/silica compounds on the thermal, flow and adhesion properties were investigated. The curing behavior was examined by differential scanning calorimetry (DSC), and the flow properties of the epoxy compounds were evaluated from penetration rate measurements. The adhesion strength as a mechanical property was determined by die shear strength testing. The silane coupling agent type had a significant effect on the thermal, flow and adhesion properties. The coefficients of thermal expansion (CTE) and adhesion of the DGEBF epoxy/SiO2 systems could be enhanced by the addition of silane coupling agents. In addition, the penetration rate was increased by the addition of a coupling agent except for the CA-A coupling agent. This was interpreted in terms of the reactive functional groups and dispersion forces resulting in coupling agents on the interfaces between the DGEBF epoxy resin and silica. (C) 2012 Elsevier B.V. All rights reserved.