The effect of dry milling processes on the surface properties of an attapulgite clay, also called palygorskite, was investigated by carrying out experiments with different types of grinding devices. Ground products were then characterized by size measurement, scanning electron microscopy, X-ray diffraction, adsorption-desorption of N-2 and inverse gas chromatography at infinite dilution (IGC-ID) as well as finite concentration conditions (IGC-PC). These analyses were performed to evaluate the changes in particle size distribution, morphology, crystallinity and surface properties of attapulgite powder, respectively. Among the tested dry grinding devices, grinding in an air jet mill (Alpine 50 AS) and a vibratory ball mill (Pulverisette 0) led to the most significant particle size reduction. SEM photomicrographs showed that a breakage of the fibrous structure took place during dry grinding. Moreover, long grinding in Pulverisette 0 resulted in the complete destruction of fibre morphology followed by agglomeration. XRD analysis showed that whatever the grinding process, the microstructure of the attapulgite was not affected. IGC confirmed that only grinding in Pulverisette 0 affected the surface properties notably. In this case, the most significant decreases were observed in the dispersive component of the surface energy (164 to 116 mJ/m(2)) and in the specific surface area obtained with the octane probe (114.5 m(2)/g to 62.6 m(2)/g) by IGC-ID and IGC-FC, respectively. At the same time, a modification of the distribution functions of the adsorption energies (DFAE), giving information about surface heterogeneity, was noticed. (C) 2014 Elsevier B.V. All rights reserved.