Thermogravimetry (TG), energy dispersive X-ray microanalysis (EDX), scanning electron microscopy (SEM), mapping surface and X-ray diffraction (XRD) were used for the study of solid-state reaction on Pt-15%Rh with electrodeposited mercury. The results suggest when heated the mercury film react with the Pt-15%Rh alloy to form intermetallics having different thermal stabilities indicated by three mass loss steps. The first mass loss step occurs between room temperature and 184 degrees C only the bulk Hg is removed and PtHg4, PtHg2 and RhHg2 were characterized by XRD. The second step, between 184 and 271 degrees C, was attributed to PtHg4 decomposition with formation of PtHg2 stabilized by RhHg2. The third step, between 271 and 340 degrees C, was attributed to decomposition of a solid-solution of PtHg2/RhHg2. The fourth step, between 340 and 600 degrees C, was ascribed to: (1) a thermal decomposition of PtHg2, formed by a PtHg eutectoid reaction (similar to 340 degrees C) on the surface and (2) Hg removal from a solid solution of Pt-15%Rh(Hg). (C) 2013 Elsevier B.V. All rights reserved.