Dye-sensitized thin film hybrid solar cells (DS thin film solar cell) were fabricated by one-pot process using solution processable zinc oxide (ZnO) precursor as electron acceptor, ester-functionalized polythiophene copolymer as donor and a squaraine dye. Incorporation of slight amount of ester functionality (6%) in the regioregular poly-3-hexylthiophene (P3HT) main chain leads to enhancement in the photoconversion efficiency of the ester functionalized polymer (P3HT-E) from 0.8% to about 1% (AM1.5, 100 mw/cm(2)). Photocurrent associated with both of the P3HT-E (400-650 nm) and the squaraine dye (650-750 nm) were observed in incident photon to current efficiency curve of the DS thin film solar cell. This proves that the ZnO/dye/P3HT-E interface could be fabricated by one-pot coating process from ternary mixture based on a ZnO precursor. (C) 2013 Elsevier B.V. All rights reserved.