Analysis of measured charge-carrier mobilities and fill factors in solution-processable small-molecule bulk-heterojunction solar cells reveals that in order to achieve a high FF, the hole and electron mobilities must be >10(-4) cm(2) V-1 s(-1). Neat-film mobility measurements are also found to be a useful predictor of the maximum blend film mobility and FF obtained in blend film solar cells.