We report for the first time hydrophobic properties on cotton fabric successfully achieved by grafting graphene oxide on the fabric surface, using a dyeing method. Graphite oxide synthesized by oxidizing natural flake graphite employing improved Hummer's method showed an inter layer spacing of similar to 1 nm from XRD. Synthesized graphite oxide was exfoliated in water using ultrasound energy to obtain graphene oxide (GO). AFM data obtained for the graphene oxide dispersed in an aqueous medium revealed a non-uniform size distribution. FTIR characterization of the synthesized GO sheets showed both hydrophilic and hydrophobic functional groups present on the nano sheets giving them an amphiphilic property. GO flakes of different sizes were successfully grafted on to a cotton fabric surface using a dip dry method. Loading different amounts of graphene oxide on the cotton fiber surface allowed the fabric to demonstrate different degrees of hydrophobicity. The highest observed water contact angle was at 143 degrees with the highest loading of graphene oxide. The fabric surfaces grafted with GO also exhibits adhesive type hydrophobicity. Microscopic characterization of the fiber surface using SEM and AFM reveals the deposition of GO sheets on the fiber surface as a conformal coating. Analysis of the fabric surface using UVvis absorption allowed identification of the ratio of hydrophobic to hydrophilic domains present on the GO coated cotton fabric surface. Hydrophobic properties on cotton fabric are ascribed to two dimensional amphiphilic properties of deposited GO nano sheets, which successfully lower the interfacial energy of the fabric surface. (C) 2014 Elsevier B.V. All rights reserved.