nanocomposites were investigated for supercapacitor application. Nanocomposites with varying weight/weight ratio of PANI and Px-MWCNT were prepared by in-situ polymerization of aniline over Px-MWCNT. Transmission and scanning electron microscopic analysis showed that the MWCNT was partial unzipped along the length of tubes. The morphology of PANI/Px-MWCNT nanocomposites exhibited wrapping of PANI over Px-MWCNT. Symmetric supercapacitors containing PANI/Px-MWCNT nanocomposites as the electrode material were fabricated. The electrochemical characterization of the nanocomposites was carried by two electrode method (unit cell configuration). Cyclic voltammetric analysis showed a synergistic increase in specific capacitance of the nanocomposites. Charge-discharge cycle study indicated that nanocomposites have greater charge-discharge rate capability than pure PANI. The observed result is attributed to the shorter diffusion length of ions in the nanocomposites as compared to that of pure PANI. The electrochemical impedance spectra of supercapacitors were resolved into real and losscapacitances. The loss capacitance indicated that the time constant of the nanocomposites decreases with increase in the Px-MWCNT content. The supercapacitors showed enhanced stability during continuous charge-discharge cycling as the PX-MWCNT content in the nanocomposites increased. PANI-50 and PANI-25 nanocomposites based supercapacitors exhibited 91% and 93% capacitive retention after 2000 charge-discharge cycle while pure PANI showed only 67% capacitance retention for the same number of cycles. (C) 2015 Elsevier Ltd. All rights reserved.