Pristine Ni/gamma-Al2O3 and CeO2-Ni/gamma-Al2O3 catalysts were prepared by co-impregnation technique for dry reforming of propane. X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM) were used to examine the structure and morphology of the catalysts before and after the reforming reactions. The excellent interaction between catalyst active phases was observed in both CeO2-Ni/gamma-Al2O3 and Ni/gamma-Al2O3 stabilized with polyethelene glycol (Ni/gamma-Al2O3-PEG). Towards C3H8 and CO2 conversion, the CeO2-Ni/gamma-Al2O3 and Ni/gamma-Al2O3 PEG showed improved catalytic activity when compared to the pristine Ni/gamma-Al2O3 catalyst. Interestingly, high H-2 concentration was achieved with the CeO2-Ni/gamma-Al2O3 and high CO concentration with the Ni/gamma-Al2O3-PEG, which is due to the nanoconfinement of nickel particles within the support and favorable metal-support interaction as a result of plasma reduction. The CeO2-Ni/gamma-Al2O3 catalyst exhibited better stability for anti-sintering and coke resistance, thus exhibiting high reactivity and durability in the dry reforming. Copyright (C) 2014, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd.