Polystyrenic (PS) anion-exchange resin and polyacrylic (PA) anion-exchange resin were used to investigate the effect of resin chemical structure on the adsorption of humic acid (HA). Due to the rearrangement of HA to form layers that function as barricades to further HA diffusion, PS resin exhibited 12.4 times slower kinetics for the initial adsorption rate and 8.4 times for the diffusion constant in comparison to that of the PA resin. An HA layer and a spherical cluster of HA can be observed on the surface of the PS and PA resins after adsorption, respectively. The considerable difference in HA adsorption between the PS and PA resins was due to the difference in molecule shape for interaction with different resin structures, which can essentially be explained by the hydrophobicity and various interactions of the PS resin. A given amount of HA occupies more positively charged sites and hydrophobic sites on the PS resin than were occupied by the same amount of HA on the PA resin. Increased pH resulted in an increase of HA adsorption onto the PA resin but a decrease in adsorption onto PS resin, as the non-electrostatic adsorption led to electrostatic repulsion between the HA attached to the resin and the HA dissolved in solution. These results suggest higher rates of adsorption and higher regeneration efficiency for interaction of HA with more hydrophilic anion exchange materials. (c) 2014 Elsevier Inc. All rights reserved.