Nanocomposites were prepared by adding 1-3 vol % multiwalled carbon nanotubes (MWCNTs) to polyamide 6 (PA6), polypropylene (PP), and their co-continuous blends of 60/40 and 50/50 volume compositions. Because of the good interaction and interfacial adhesion to the PA6, nanotubes were disentangled and distributed evenly through nanocomposites containing PA6. In contrast, lack of active interactions between the matrix and the CNTs resulted in poor tube dispersion in PP. These observations were then verified by studying the rheology and electrical conductivity of their respective nanocomposites. Absence of percolated CNT clusters and possible wrapping of the tubes by PA6 resulted in low electrical conductivity of PA6/CNT nanocomposites. On the other hand, despite the weak dispersion of the tubes, electrical conductivities of PP/CNT nanocomposites were much higher than all other counterparts. This could be the result of good three-dimensional distribution of the agglomerated bundles and secondary aggregation of tubes in PP. Adding CNTs to blends of PA6/PP (60/40 and 50/50) resulted in almost full localization of carbon nanotubes in PA6, leading to their higher effective concentration. At the same CNT loadings, the blend nanocomposites had three to seven orders of magnitude higher electrical conductivity than pure PA6. (c) 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015, 53, 368-378