Multiferroic materials have been the subject of intense study, but it remains a great challenge to synthesize those presenting both magnetic and ferroelectric polarizations at room temperature. In this work, we have successfully obtained LiNbO3-type ScFeO3, a metastable phase converted from the orthorhombic perovskite formed under 15 GPa at elevated temperatures. A combined structure analysis by synchrotron X-ray and neutron powder diffraction and high-angle annular dark-field scanning transmission electron microscopy imaging reveals that this compound adopts the polar R(3)c symmetry with a fully ordered arrangement of trivalent Sc and Fe ions, forming highly distorted ScO6 and FeO6 octahedra. The calculated spontaneous polarization along the hexagonal c-axis is as large as 100 mu C/cm(2). The magnetic studies show that LiNbO3-type ScFeO3 is a weak ferromagnet with TN = 545 K due to a canted G-type antiferromagnetic ordering of Fe3+ spins, representing the first example of LiNbO3-type oxides with magnetic ordering far above room temperature. A comparison of the present compound and rare-earth orthorhombic perovskites RFeO3 (R = La-Lu and Y), all of which possess the corner-shared FeO6 octahedral network, allows us to find a correlation between TN and the Fe-O-Fe bond angle, indicating that the A-site cation-size-dependent octahedral tilting dominates the magnetic transition through the Fe-O-Fe superexchange interaction. This work provides a general and versatile strategy to create materials in which ferroelectricity and ferromagnetism coexist at high temperatures