This paper focuses on novel iron-based soft magnetic composites synthesis utilizing low friction factor parylene C films to coat iron powder via chemical vapor deposition polymerization. The morphology, magnetic properties, density, and chemical stability of parylene insulated iron particles were investigated. The coated parylene insulating layer was characterized by scanning electron microscopy and energy dispersive X-ray spectroscopy. The thickness of parylene C film is averagely 300 nm according to the results of transmission electron microscopy. Parylene C film uniformly coated the powder surface resulting in reducing the permeability imaginary part, increasing electrical resistivity and increasing the operating frequency of the synthesized magnets. It was shown that the parylene C coated compacts exhibited noticeably higher density compared to the epoxy resin coated compacts at the same pressure, suppress at 800 MPa increased the density by 17.02%. The result of Tafel curves indicated that the resistance of the iron particles to corrosion by NaCl solution is obviously improved after being insulated with parylene C film. (C) 2015 Elsevier B.V. All rights reserved.