A novel positively charged loose nanofiltration (NF) membrane was fabricated feasibly by UV-induced photografting polymerization of diallyl dimethyl ammonium chloride (DADMAC) on Polysulfone ultrafiltration membrane. A possible reaction mechanism was proposed that a linear chain structure and/or pyrrole like five-membered nitrogen heterocycles structure on the side chain were grafted to form the active barrier layer. NF membrane demonstrated a looser average pore size of 8.6 nm and positive charges surface. Owing to the nanoscale ultrathin nanoscale barrier layer and the combination of Donnan exclusion and steric hindrance, NF membrane exhibited good hydrophilicity, a high pure flux of 60 L/m(2) h (0.5 MPa), a good salt rejection to Mg2+ (90.8%), Al3+ (94.0%), Ca2+ (91.5%), and a high dye rejection to methylene blue (99.4%) and congo red (100.0%) respectively. The salts rejection of NF membrane to different salts followed the order of AlCl3 > CaCl2 > MgCl2 > NaCl > LiCl> MgSO4 > Na2SO4 NF membrane showed certain fouling resistance to seawater and BSA solution. The grafting polymerization kinetics were comprehensively investigated including irradiation time, monomer concentration and irradiation intensity. X-ray Photoelectron Spectroscopy (XPS), scanning electron microscopy (SEM), atomic force microscopy (AFM) and contact angle measurement were employed to investigate membrane chemistry, morphologies, and hydrophilicity. (C) 2014 Elsevier B.V. All rights reserved.